导致阳光板裂开的原因是什么?

来源:http://www.wanzhongyue.com/ 日期:2019-02-26 发布人:admin 浏览次数:

作为阳光板厂家-,时常会听见有客户这样谈论,pc阳光板很容易就裂开了,不经用,不实用,其实不然,今天就和大家总结下九点会导致阳光板裂开的原因:
As a manufacturer of sunshine panels, we often hear customers talking about it. The PC sunshine panels are easy to crack. They are useless and not practical. In fact, otherwise, today we will sum up the reasons why the nine points will cause the sunshine panels to crack.
阳光板开裂原因总结
Summary of the Causes of Sunshine Plate Cracking
1、加工的刀具或东西皆不得对板材的非加工部位构成任何危害,切断有必要润滑。因为细微的危害也会致使严峻的开裂。
1. Tools or things processed shall not cause any harm to the non-processed parts of the sheet. It is necessary to lubricate the cut-off part. Because minor hazards can also lead to severe cracks.
2、在设备完结之前不得损坏或揭掉保护膜,以避免擦伤外表。
2. The protective film should not be damaged or removed before the equipment is finished to avoid abrasion.
3、绝不允许把pc阳光板直接钉在骨架上,不然会因为板材的胀大发生很高的应力并损坏穿孔边际处。
3. It is absolutely not allowed to nail the PC sunshine plate directly to the skeleton, otherwise, high stress will occur due to the expansion of the plate and damage the perforation margin.
4、有必要选用适用于聚碳酸酯塑料的密封胶和密封胶垫。在湿式装置系统中要运用湿式的密封胶膏。
4. It is necessary to select sealants and gaskets suitable for polycarbonate plastics. Wet sealant should be used in wet installation system.
5、若弯曲的板材曲率半径太小的话,板材的机械强度和抗化学性都会急剧下降,为了避免露出于外的那面发生风险的应力开裂,板材弯曲的半径不得小于规则的数据。
5. If the curvature radius of the bending plate is too small, the mechanical strength and chemical resistance of the plate will decrease sharply. In order to avoid the risk of stress cracking on the exposed side, the bending radius of the plate should not be less than the regular data.
6、pc阳光板忌讳接触碱性物质及有侵蚀性的有机物质,如碱、碱式盐、醛、酯、醚、酚、卤代烃、芳香烃、甲醇、异丙醇、沥青等。这些物质均会致使极严峻的化学应力开裂。
6. The PC solar panel should avoid contacting alkaline substances and corrosive organic substances, such as alkali, alkaline salts, aldehydes, esters, ethers, phenols, halogenated hydrocarbons, aromatic hydrocarbons, methanol, isopropanol, asphalt, etc. These substances can cause extremely severe chemical stress cracking.
7、pc多层板材绝不能垂直于肋条的方向进行弯曲,因这么将不能发生曲面桁条效应,且在应力效果下,促进把板压扁乃至开裂。板子有必要顺着肋条的方向进行弯曲。
7. Multilayer PCs must not bend perpendicular to the direction of ribs, because it will not produce curved surface truss effect, and in the stress effect, it will promote the flattening and cracking of the plates. It is necessary for the board to bend in the direction of the ribs.
8、运送、贮存时有必要妥善衬垫、包装、平放,因为板材外表上遭到任何细微的危害(如划痕)都将开展成裂口。
8. It is necessary to properly pad, pack and lay down when transporting and storing, because any minor hazards (such as scratches) on the exterior of the sheet will develop into cracks.
9、购买了价格便宜的收回料制作的残次pc阳光板。
9. Purchase of cheap recycled materials made of residual PC solar panels.
上述信息是我们济南阳光板整理发布希望对大家有所帮助我们的网站是:http://www.wanzhongyue.com
The above information is our Jinan Sunshine Plate Release Hope to help you with our website is: http://www.wanzhongyue.com!
相关新闻


  天桥区巨龙采光板经销处            联系人:万经理            座机:15806664558
 手机:15806664558        15066129603       
  技术支持: 济南诺商   鲁ICP备14016125号 网站地图 XML TXT

统一服务热线

15806664558 

鲁公网安备 37010502001033号

【本站图片均由网站所有方提供,部分图片来源于网络,如无意中侵犯了某媒体或个人的知识产权,请来信或来电告之,本网站将立即删除。】