阳光板开裂的原因是什么

来源:http://www.wanzhongyue.com/ 日期:2019-04-02 发布人:admin 浏览次数:

  作为阳光板厂家,时常会听见有客户这样议论,pc阳光板很容易就裂开了,不耐用,不实用,其实不然,今天就和大家总结下九点会导致阳光板裂开的原因:
  As a sunplate manufacturer, we often hear such comments from customers. The PC sunplate is easy to crack. It is not durable and practical. In fact, otherwise, today we will sum up the reasons why the sunplate will crack at 9:00:00:00:00:00:00:00:00:00:00.
  阳光板开裂原因总结
  Summary of the Causes of Sunshine Plate Cracking
  1、加工的刀具或东西皆不得对板材的非加工部位形成任何损害,切口有必要润滑。由于细微的损害也会致使严峻的开裂。
  1. Tools or things processed shall not cause any damage to the non-processed parts of the sheet. It is necessary to lubricate the incision. Because of minor damage can also lead to severe cracking.
  2、在装置完结之前不得损坏或揭掉保护膜,以防止擦伤外表。
  2. The protective film should not be damaged or removed before the device is finished to prevent abrasion.
  3、绝不允许把pc阳光板直接钉在骨架上,不然会由于板材的胀大发作很高的应力并损坏穿孔边际处。
  3. It is absolutely not allowed to nail the PC sunshine plate directly to the skeleton, otherwise, the high stress will occur due to the expansion of the plate and damage the perforation margin.
  4、有必要选用适用于聚碳酸酯塑料的密封胶和密封胶垫。在湿式安装体系中要使用湿式的密封胶膏。
  4. It is necessary to select sealants and gaskets suitable for polycarbonate plastics. Wet sealant should be used in wet installation system.
  5、若曲折的板材曲率半径太小的话,板材的机械强度和抗化学性都会急剧下降,为了防止露出于外的那面发作危险的应力开裂,板材曲折的半径不得小于规定的数据。
  5. If the curvature radius of the tortuous sheet is too small, the mechanical strength and chemical resistance of the sheet will drop sharply. In order to prevent dangerous stress cracking on the exposed side, the tortuous radius of the sheet should not be less than the prescribed data.
  6、pc阳光板忌讳触摸碱性物质及有侵蚀性的有机物质,如碱、碱式盐、醛、酯、醚、酚、卤代烃、芳香烃、甲醇、异丙醇、沥青等。这些物质均会致使极严峻的化学应力开裂。
  6. It is taboo to touch alkaline substances and corrosive organic substances, such as alkali, alkaline salts, aldehydes, esters, ethers, phenols, halogenated hydrocarbons, aromatic hydrocarbons, methanol, isopropanol, asphalt, etc.  These substances can cause extremely severe chemical stress cracking.
  7、pc多层板材绝不能垂直于肋条的方向进行曲折,因这么将不能发作曲面桁条效应,且在应力效果下,促进把板压扁甚至开裂。板子有必要顺着肋条的方向进行曲折。
  7. Multilayer PCs must not bend perpendicular to the direction of ribs, because this will not occur surface truss effect, and in the stress effect, promote the flattening or even cracking of the plate. It is necessary for the board to zigzag in the direction of the ribs.
  8、运送、贮存时有必要妥善衬垫、包装、平放,由于板材外表上遭到任何细微的损害(如划痕)都将开展成裂口。
  8. It is necessary to properly pad, pack and lay down when transporting and storing. Any minor damage (such as scratches) on the surface of the sheet will develop into cracks.
  9、购买了价格便宜的回收料制造的劣质pc阳光板。
  9. Purchased cheap recycled materials to manufacture inferior PC sunpanels.
  阳光板厂家建议
  Suggestions from Sunplate Manufacturers
  在选用阳光板时,不能贪图小便宜,去买市面上廉价(您感觉赚到了)的劣质阳光板,安装时请专业安装人员严格按照阳光板厂家给的安装建议。
  When choosing sunboard, you should not be greedy for a small price to buy cheap (you feel you have earned) inferior sunboard on the market. When installing, professional installers should strictly follow the installation suggestions given by the sunboard manufacturer.
相关新闻


  天桥区巨龙采光板经销处            联系人:万经理            座机:15806664558
 手机:15806664558        15066129603       
  技术支持: 济南诺商   鲁ICP备14016125号-1 网站地图 XML TXT

统一服务热线

15806664558 

鲁公网安备 37010502001033号

【本站图片均由网站所有方提供,部分图片来源于网络,如无意中侵犯了某媒体或个人的知识产权,请来信或来电告之,本网站将立即删除。】